Unit | Value | ||
---|---|---|---|
Recoil Permeability | / | 1.05 | |
Curie Temp. | ℃ | 310-350 | |
Max. Working Temp, | ℃ | 80-230 | |
Rever. Temp. Coeff. of Br | %/℃ | -0.13 to -0.09 | |
Rever. Temp. Coeff. of Hcj | %/℃ | -0.70 to -0.45 | |
Density | g/㎤ | 7.4-7.6 | |
Vickers Hardness | Hv | 560-600 | |
Elasticity Modulus | kN/㎟ | 140-170 | |
Flexural Strength | kgf/㎟ | 2500-3000 | |
Compressive Strength | kgf/㎟ | 9000-10000 | |
Coeff. of Thermal Expansion | ( C┴ ) | 10 /℃ | -2 to 0 |
( C║ ) | 10 /℃ | 4-9 | |
Specific Electric Resistance | 10-6Ω.m | 1.3-1.6 | |
Specific Heat Capacity | J/(kg.℃) | 350-500 | |
Thermal Conductivity | W/(m.℃) | 5-15 |
※ 아래 테이블을 좌우로 이동하세요.
Suggested Environment Temperature | Coating Thickness | Salty Spray Test | Salty Spray Test | Pressure Cooker Test | Temperature & Humidity Test | Resistance of Weak Acid & Weak Alkali | Resistance of solvent | Comments |
---|---|---|---|---|---|---|---|---|
Phosphorization | < 80℃ | < 1μm | Worse | Not Available | 24 Hours Very Poor |
Very poor | Very poor | Protection for temporary storage and short term transportation. |
Blue &White Zn | < 150℃ | 17-15μm | > 24 hours | Not Available | 24Hours Very Poor |
Poor | Poor | Poor protective capability, only for common environment |
Rainbow Zn | < 150℃ | 7-15μm | > 48 hours | Not Available | 48Hours Very Poor |
Fair | Fair | With good protective capability for moisture, hot and industrial environment. |
Ni | < 200℃ | 10-20μm | > 24 hours | Fair | Fair | Fair | Good | For general protection purpose and suitable for most kinds environment. |
Ni+Ni | < 200℃ | 15-25μm | > 48 hours | Good | Good | Fair | Good | Better corrosion resistance than Ni coating, suitable for dew atmosphere and long time using. |
Ni+Cu+Ni | < 200℃ | 15-25μm | > 72 hours | Very Good |
Very Good | Fair | Good | BThe most popular coating type. Corrosion resistance is better than Ni+Ni coating. |
Epoxy / Ni+Cu+Epoxy | < 130℃ | 15-25μm | > 96 hours | Not Available | Good | Very Good | Poor | Special for requirement of electric insulation& environment of strongly industrial corrosion. |
Ni+Sn | < 150℃ | 15-25μm | > 72 hours | Not Available | Very Good | Fair | Good | Superior resistance to humid atmosphere even better than Ni+Cu+Ni |
Spray Coated Al | < 200℃ | 5-10μm | > 288 hours | Not Available | Very Good | Fair | Good | Superior resistance to salt and humid atmosphere, suitable for coating big size &anomalous magnet |
Ion Vapor Deposited Al | < 400℃ | 10-30μm | > 288 hours | Very Good |
Very Good | Fair | Good | Same protecting role as spray coated Al. even coating layer with excellent adhesion on magnet. |
Ni+Cu+Ni plus EVERLUBE | < 100℃ | 15-30μm | > 120 hours | Better than Ni+Cu+Ni | Very good About 500hours | Very Good | Better Than Epoxy | resistance to corrosion &wearing, good chemical stability, special for engineering usage. |